Ce que nous faisons
Layer thickness 25 to 50 µm
Layer thickness 25 to 50 µm
Surface hardness up to 500 HV
Surface hardness up to 500 HV
Excellent wear and galling resistance
Excellent wear and galling resistance
Better electrical insulation than Type II
Better electrical insulation than Type II
Available in black and dark tones
Available in black and dark tones
Suitable
Suitable for pneumatic and hydraulic parts
Matériaux
| Aluminium 6061 |
| Aluminium 7075 |
| Aluminium 2024 |
| Cast and forged aluminium |
Spécifications clés
| Spécification | Détails |
|---|---|
| Thickness | 25–50 µm |
| Hardness | up to 500 HV |
| Colour | Black, dark grey, natural |
| Dielectric strength | High, insulating |
| Growth | Approximately half the layer thickness |
| Lead time | 4–7 working days |
Finitions de surface & post-traitement
Sealed or unsealed depending on application
Sealed or unsealed depending on application
Machined after coating for critical fits
Machined after coating for critical fits
PTFE impregnation for low friction
PTFE impregnation for low friction
Questions fréquentes
Where is hard anodizing essential?
On aluminium surfaces that slide, rotate or seal: cylinder bores, valve spools, wear plates and guides. Without it, soft aluminium galls and wears quickly.
Can hard anodized parts be machined afterwards?
Yes, but only on masked or uncoated areas, or by diamond grinding. Because the coating is very hard, we plan the process so critical fits are either masked or finished after coating.
Is it suitable for food contact?
Sealed hard anodizing is used in food processing equipment, but you should confirm the specific application against the relevant standard before production.
More in this section
Anodizing
Type II and Type III anodizing for aluminium: clear, black and colour finishes with improved corrosion and wear resistance, thickness from 5 to 50 µm.
Bead Blasting
Glass bead blasting for a uniform satin finish on metal and plastic parts. Hides tool marks, prepares surfaces for coating and gives a premium matte look.
Sand Blasting
Sand blasting for surface cleaning, descaling and roughening. Removes rust, scale, old coating and oxide before welding, painting or bonding.
Polishing
Mechanical polishing to mirror and optical finishes: Ra down to 0.05 µm for mould cavities, light guides, medical parts and decorative surfaces.
Powder Coating
Powder coating in RAL and Pantone colours: durable, thick and impact-resistant finish for sheet metal and fabrications, from 60 to 120 µm.
Prêt à lancer votre projet de {service} ?
Envoyez vos fichiers aujourd'hui — devis vérifié DFM sous 24 heures.